Hardox 500 Tuf General Product Description

In which thicknesses is Hardox 500 Tuf produced?

Hardox® 500 Tuf roll unwinding Mechanical properties

Hardox® 500 Tuf Plate Mechanical Properties

Hardox® 500 Tuf Decoiling Sheets Impact Properties

Hardox® 500 Tuf Plate Impact Properties

Hardox 500 Tuf General Product Description


Sacdan Adam has Hardox 500 Tuf in stock. You can send us a whatsapp message immediately by clicking the message icon at the bottom right.

Hardox 500 Tuf is a new generation Hardox wear plate.

The Hardox® 500 Tuf wear plate is the latest upgrade in the Hardox product range. (2022)It offers high strength, exceptional hardness and guaranteed toughness in a single wear plate. Hardox® 500 Tuf combines the best features of Hardox® 450 and Hardox® 500. The resulting wear plate has no real competitor on the market.

In which thicknesses is Hardox 500 Tuf produced?


Hardox® 500 Tuf is available in thicknesses between 4.0 - 25.4 mm as plate and between 3.0 - 6.5 mm as sheet. Detailed information about the sizes is given in the size programme.

Download the size programme as pdf.

Hardox® 500 Tuf unwinding from roll Mechanical properties

 
THICKNESS (mm) 3.0 - 6.5
HARDNESS 1) (HBW) 475 - 505
TYPICAL Yield Strength 1250 (MPa), NOT GUARANTEED


 
Hardox® 500 Tuf Plate Mechanical Properties


THICKNESS (mm) 4.0 - 25.4
HARDNESS 1) (HBW) 475 - 505
TYPICAL Yield Strength 1250 MPa), NOT GUARANTEED
 
1) Brinell hardness, HBW according to EN ISO 6506-1 on a machined surface 0,5-3 mm below the surface. cast and at least one test specimen per 40 tonnes. The nominal thickness of the delivered plates shall not deviate by more than +/- 15 mm with respect to the thickness of the test specimen used for the hardness test. The Brinell hardness test for sheet metal is performed according to EN ISO 6506-1 on each heat treatment. individual/coil. The hardness is measured on a milled surface 0.3 - 2 mm below the surface.


 
Hardox® 500 Tuf Uncoiled Sheets Impact Properties


CROSS-TESTED, GUARANTEED IMPACT ENERGY,
CHARPY V 10X10 MM TEST SAMPLE. 1)
27 J / -40 °C

 
Hardox® 500 Tuf Plate Impact Properties


CROSS-TESTED, GUARANTEED IMPACT ENERGY,
CHARPY V 10X10 MM TEST SAMPLE. 1)
27 J / -20 °C
1) Impact testing was carried out at thicknesses ≥ 6 mm for plate and ≥ 3 mm for sheet metal. For thicknesses between 3 and 11.9 mm, sub-size Charpy V-samples were used. The minimum value determined is proportional to the cross-sectional area of the sample when compared to a previously full-size sample (10 x 10 mm). Impact test according to ISO EN 148 for each heat and thickness group. Average of three tests.